Transactions of the INDIAN CERAMIC SOCIETY   Vol. 76  2017
Regeneration of HA Coating on Porous ZrO2 Gradient Bioceramics
Junwei Wu,1 Xiao Wang,1 Chunyan Wang,1 Xicheng Wei1, * and Renfu Quan2
Pages : 252-257
DOI : 10.1080/0371750X.2017.1412838
Abstract
Themal decomposition and poor mechanical strength of hydroxyapatite (HA) restrict its further application in the field of bone tissue engineering. A porous HA/ZrO2 gradient bioceramics with regenerated HA coating was thus designed. Its porosity reached about 70% with its compressive strength reaching about 14 MPa. The porosity and mechanical strength were balanced appropriately by immersing the bioceramics for three times using slurry concentrations of 60%, 55% and 50%, respectively. Through analyzing the decomposition and regeneration behaviour of HA by DSC, Raman and XRD, 4 mol mass of NaHCO3 heated at 900oC for 2 h was the optimum condition for regenerating HA coating. The regeneration effect and process were also discussed. [Keywords: Hydroxyapatite, Zirconia, Porosity, Regeneration, Biocompatibility]
Full text : Subscribe to Download Full Text
[Go Back]
 
MAIN PAGE | SITE MAP | PRIVACY POLICY | TERMS & CONDITIONS  | CONTACT US | FEEDBACK
Copyright Protected 2008, The Indian Ceramic Society. All right reserved.

Developed By : Hi-Tech Soft & Multimedia